TY  - JOUR
T1  - Формирование монокристаллических наноструктур оксида цинка на подложках ниобата лития и на металлических пленках
JF  - Известия Национальной академии наук Беларуси. Серия физико-технических наук
AU  - Пашкевич Г. А., 
AU  - Орлов А. Т., 
AU  - Ульянова В. А., 
AU  - Богдан А. В., 
Y1  - 2025-03-11
UR  - https://www.academjournals.by/publication/13785
N2  - The results of the rod nanostructures synthesis and porous zinc oxide films on lithium niobate substrates by hydrothermal method and on the metal films by electrochemical deposition are presented. It was shown that hydrothermal method can be successfully used for formation of the hexagonal rod structures with a diameter up to 100 nm on the single crystal substrates. Electrochemical synthesis method is promising for formation of zinc oxide rod structures with a diameter up to 1 ^m on gold films and porous films on aluminum conductive layers. It was established that increasing of the solution concentration for the electrochemical synthesis method increases diameter of zinc oxide rod nanostructures. The obtained results can be used to select the optimal process parameters of zinc oxide nanostructures synthesis for subsequent application in micro-, nanoelectronics and photovoltaics